| 项目 Properties | 望位 Unit | 檢驗方法 Test Method | 標準級 Standard | 耐候级 Weather-Resistant | 低模垢级 Low Molding Deposits | 低甲醛氣析出级 Low Voc | ||||||
| FM025 | R6 | FM090 | FM130 | FM270 | FM450 | R6UV | FM090 UV | FM090 LMD | FM090 LV | |||
| 熔融指數 Melt Index | g/10min | ISO 1133 | 2.5 | 6 | 9 | 13 | 27 | 45 | 6 | 9 | 9 | 9 |
| 密度 Density | g/cm 3 | ISO 1183 | 1.41 | 1.41 | 1.41 | 1.41 | 1.41 | 1.41 | 1.41 | 1.41 | 1.41 | 1.41 |
| 硬度 Rockwell Hardness | M | ISO 2039-2 | 78 | 80 | 80 | 80 | 80 | 80 | 80 | 80 | 80 | 80 |
| 抗折強度 Flexural Strength | MPa | ISO 178 | 82 | 86 | 88 | 88 | 90 | 90 | 86 | 88 | 88 | 88 |
| 抗折彈性像数 Flexural Modulus | MPa | ISO 178 | 2400 | 2450 | 2500 | 2500 | 2550 | 2550 | 2450 | 2500 | 2500 | 2500 |
| 立伸強度(降伏點) ensile Strength (at yield point) | MPa | ISO 527-2/1A | 60 | 62 | 62 | 62 | 63 | 63 | 62 | 62 | 62 | 62 |
| 延伸率(斷裂點) Tensile Elongation (at break point) | % | ISO 527-2/1A | 40 | 38 | 35 | 35 | 30 | 20 | 38 | 35 | 35 | 35 |
| 簡支樑缺口衝擊強度 Charpy Impact Strength (notched) | KJ/m ² | ISO 179-1, 179-2 | 8 | 7 | 6.5 | 6 | 5.5 | 4.5 | 7 | 6.5 | 6.5 | 6.5 |
| 吸水率 Water Absorption(23℃,50%RH) | % | ISO 62 | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 |
| 阻燃性 Flammability | - | UL94 | HB | HB | HB | HB | HB | HB | HB | HB | HB | HB |
| 成型收縮率 Mold Shrinkage | % | ISO 294-4 | 1.8-2.2 | 1.8-2.2 | 1.8-2.2 | 1.8-2.2 | 1.8-2.2 | 1.8-2.2 | 1.8-2.2 | 1.8-2.2 | 1.8-2.2 | 1.8-2.2 |
| 熱變形溫度 Heat Deflection Temperature 1.80 Mpa | °C | ISO 75-1,-2 | 100 | 103 | 103 | 102 | 102 | 100 | 103 | 103 | 103 | 103 |
| 線膨脹係數 Linear Expansion Factor | x10^(-5) /°C | ISO 11359-2 | 12 | 12 | 12 | 11 | 11 | 11 | 12 | 12 | 12 | 12 |
| 熔點 Melting Point | °C | ISO 11357-3 | 165 | 165 | 165 | 165 | 165 | 165 | 165 | 165 | 165 | 165 |
| 體積電阻率 Volume Resistivity | Ω.cm | IEC 60093 | 1x10^(14) | 1x10^(14) | 1x10^(14) | 1x10^(14) | 1x10^(14) | 1x10^(14) | 1x10^(14) | 1x10^(14) | 1x10^(14) | 1x10^(14) |
| 表面電阻率 Surface Resistivity | Ω | IEC 60093 | 1x10^(16) | 1x10^(16) | 1x10^(16) | 1x10^(16) | 1x10^(16) | 1x10^(16) | 1x10^(16) | 1x10^(16) | 1x10^(16) | 1x10^(16) |
| 絕緣破壞强度(3mm) Dielectric Breakdown Strength(3mm) | kV/mm | IEC60243-1 | 19 | 19 | 19 | 19 | 19 | 19 | 19 | 19 | 19 | 19 |
| 特性 Features | 高黏度 High-viscosity | 標準增韌 Standard toughness | 標準流動 Standard flow | 中流動 Medium-flow | 高流動 High-flow | 超高流動 Superhighflow | 耐候性佳 WeatherResistant | 耐候性佳 WeatherResistant | 模垢比FM090低 Less molding deposit than FM090 | 低甲醛氣析出 Low VOC | ||
| 用途 Applications | 可用於押出及射出 成型 For Extrusion and Injection molding | 韌性需求優於 FM090 Used in higher tougness than FM090 | 一般射出用規格 For general molding | 流動需求略高於 FM090 Used in higher demand for fluidity than FM090 | 用於小尺寸產品 Used to produce the small parts | 用於小尺寸零件及 薄製品 Used to ptoduce the thin or small parts | 耐候級可應用於戶外製品，具有良好的耐候性 質 Outdoor or other products requiring good weather-resistant properties. | 適用於易產生模垢的加 工狀況 Suitable for processing conditions prone to mold deposits | 適用於易有瓦斯氣產生 的加工條件 Suitable for processing conditions prone to gas generation | |||
| 扣具 Buttons, 按扣 Press-in fasteners, 管件 Plumbing, 五金 Hardware, 家用電器 Household appliances parts, 電子零件 Electronic parts, 汽車零件 Automotive, 齒輪Gears, 軸承 Bearing, 拉鏈 Zippers | ||||||||||||